specification ? ?? ? supplier : samsung electro-mechanics ? ?? ? samsung p/n : CL03C0R6BA3GNNC ? ?? ? product : multi-layer ceramic capacitor ? ?? ? description : cap, 0.6 ? ?? ? , 25v, 0.1 ? ?? ? , c0g, 0201 cl 03 c 0r6 b a 3 g n n c ? ? ? ? ? ? ? ? ?? ? ? series samsungmultilayerceramiccapacitor ? size 0201 (inchcode) l: 0.6 0.03 mm w: 0.03 mm ? dielectric c0g inner electrode ? capacitance 0.6 ? termination ? capacitance 0.1 ? plating (pbfree) tolerance product normal ? rated voltage 25 v special reservedforfutureuse ? thickness 0.3 0.03 mm ? ?? ? packaging cardboardtype,7"reel b. samsung reliablility test and judgement conditioncapacitance withinspecifiedtolerance 1 ? 10% 0.5~5vrms q 412 min insulation 10,000mohmor500mohm ? ? ratedvoltage 60~120sec. resistance whicheverissmaller appearance noabnormalexteriorappearance microscope( 10) withstanding nodielectricbreakdownor oftheratedvoltage voltage mechanicalbreakdown temperature c0g characterisitcs (from55 to125 ,capacitancechangeshoudbewithin30ppm/ ) adhesive strength nopeelingshallbeoccuronthe 200g ? f,for101sec. of termination terminalelectrode bending strength capacitancechange: bendingtothelimit(1mm) within5%or0.5 ? whicheverislarger with1.0mm/sec. solderability morethan75%ofterminalsurface snag3.0cu0.5solder istobesolderednewly 2455 ,30.3sec. (preheating:80~120 for10~30sec.) resistance to capacitancechange: solderpot:2705 ,101sec. soldering heat within2.5%or0.25 ? whicheverislarger tan ,ir:initialspec. a. samsung part number performance test condition 300% sn100% cu cu 0.3
vibration test capacitancechange: amplitude:1.5mm within2.5%or0.25 ? whicheverislarger from10 ? to55 ? (return:1min.) tan,ir:initialspec. 2hours 3direction(x,y,z) moisture capacitancechange: withratedvoltage resistance within7.5%or0.75 ? whicheverislarger 402 ,90~95%rh,500+12/0hrs q: 102 min ir: 500mohmor25mohm ? ? whicheverissmaller high temperature capacitancechange: with oftheratedvoltage resistance within3%or0.3 ? whicheverislarger max.operatingtemperature q: 206 min 1000+48/0hrs ir: 1000mohmor50mohm ? ? whicheverissmaller temperature capacitancechange: 1cyclecondition cycling within2.5%or0.25 ? whicheverislarger min.operatingtemperature 25 tan,ir:initialspec. max.operatingtemperature 25 5cycletest c. recommended soldering method : reflow(reflowpeaktemperature:260+0/5 ,10sec.max) *forthemoredetailspecification,pleaserefertothesamsungmlcccatalogue. performance test condition 200%
|